دانلود Preparation of nano-titanium dioxide from ilmenite using sulfuric acid-decomposition by liquid phase method

Abstract

In this study, high purity nano-TiO₂ was prepared from Panzhihua ilmenite using sulfuric acid-decomposition by liquid phase method. The effects of H₂SO₄ molar volume, reaction time, initial pre-heating temperature and H₂SO₄ concentration on the decomposition rate of ilmenite were investigated in detail. The results showed that the decomposition rate reached 95.21% under the optimal conditions. The resulting titanium solution was qualified with 121 g/L Ti⁴⁺. Since the initial pH value of hydrolysis system was below 3, the precipitation of metatitanic acid was obtained by direct hydrolysis of the titanium solution. On the other hand, the well-crystallized anatase and rutile were achieved at different calcination temperatures. The purity of the asprepared TiO₂ was above 99% with an average particle size of about 40–100 nm. The ilmenite ore, intermediates and final products were characterizedby X-ray diffraction (XRD), scanning electronmicroscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), energy dispersive X-ray fluorescence spectrometer (EDS), X-ray fluorescence spectroscopy (XRF), thermal gravimetric analysis (TG), inductive coupled plasma emission spectrometer (ICP) and spectrophotometer. The results demonstrated that the process was suitable for industrial production because it was inexpensive, environment-friendly and promising in the preparation of high purity nano-TiO₂.